Pancake Coil Copper Tube
C35330 DZR Brass (CW511L)
Short Description:
CDA3533, CDA486, AS-352, Q214åÊ
Cu-Zn alloys containing more than 15% Zn are susceptible to a dealloying process called Dezincification where the selective removal of Zn leaves a relatively porous and weak layer of Cu and Cu oxide. Corrosion of a similar nature continues beneath the primary corrosion layer resulting in gradual replacement of sound brass by weak, porous copper. Unless arrested this corrosion mechanism eventaully penetrates the metal, weakening it structurally and allowing liquids or gasses to leak through this porous mass.
Additions of As (typically 0.02 - 0.25%) to alpha brasses effectively produces high resistance to dezincification at normal operating temperatures. A further addition of Sn (up to 1.5%) further enhances resistance to dezincification and has led to the development of Naval brasses with good resistance in marine environments.
Send email to us
Download as PDF
| Technical Specifications: Bronze, Copper & Brass Coils | |||
| Parameter | Bronze Coil (C51000 / C52100) | Copper Coil (C11000 / C12200) | Brass Coil (C26000 / C26800) |
| Material Type | Phosphor Bronze | Electrolytic Tough Pitch (ETP) / Phosphorus Deoxidized | Cartridge Brass / Yellow Brass |
| Standard | ASTM B103 / B465 | ASTM B152 / B11 | ASTM B36 / B587 |
| Coil Form | Strip / Sheet in Coil | Strip / Sheet in Coil, Rolled | Strip / Sheet in Coil |
| Thickness Range | 0.002" to 0.128" (0.05 mm to 3.25 mm) | 0.002" to 0.250" (0.05 mm to 6.35 mm) | 0.002" to 0.128" (0.05 mm to 3.25 mm) |
| Width Range | 0.100" to 24" (2.5 mm to 610 mm) | 0.250" to 48" (6 mm to 1220 mm) | 0.250" to 36" (6 mm to 915 mm) |
| Coil Inner Diameter (ID) | 12" to 24" (305 mm to 610 mm) | 12" to 24" (305 mm to 610 mm) | 12" to 24" (305 mm to 610 mm) |
| Coil Outer Diameter (OD) | Up to 60" (1524 mm) | Up to 60" (1524 mm) | Up to 48" (1220 mm) |
| Coil Weight | 200 – 3,000 lbs (90 – 1,360 kg) | 500 – 10,000 lbs (225 – 4,500 kg) | 300 – 4,000 lbs (135 – 1,800 kg) |
| Temper Condition | Soft (O60), Half-Hard (H02), Hard (H04), Spring (H08) | Soft (O60), Half-Hard (H58), Hard (H80) | Soft (O60), Half-Hard (H02), Hard (H04), Spring (H08) |
| Corrosion Resistance | Excellent (marine / saltwater) | Excellent | Good |
| Typical Applications | Spring contacts, switch blades, connectors, bellows, fuse clips, gaskets, EMI shielding | Roofing flashing, electrical bus bars, grounding strips, gaskets, transformer windings, heat exchanger fins | Ammunition components, radiator fins, lock hardware, decorative trim, musical instrument reeds, key stock, stampings |