C2680/C2700 Brass Tube

Short Description:


Send email to us Download as PDF

Specifications

End Product

Specification

Bolt

ASTM F468

Nuts

ASTM F467

Rod

SAE J463, J461

Screws

ASTM F468

Studs

ASTM F468

Tube

ASTM B135

Tube, Welded

ASTM B587

Wire

AMS 4712, 4713, ASTM B134, SAE J463, J461

Wire, Tinned

AMS 4710

 

Chemical Composition


CU

FE

PB

ZN

Min/Max

63.0 - 68.5

0.07

0.09

Rem

Nominals

65.0000

-

-

35.0000

 

Temper

PRODUCT TYPE

TEMPER TYPE

Bolt

ASTM F468

Nuts

ASTM F467

Rod

SAE J463, J461

Screws

ASTM F468

Studs

ASTM F468

Tube

ASTM B135

Tube, Welded

ASTM B587

Wire

AMS 4712, 4713, ASTM B134, SAE J463, J461

Wire, Tinned

AMS 4710

 

Mechanical Properties

TEMPER

SECT. SIZE

COLD WORK

TYPE MIN

TEMP

TENSILE STRENGTH

YS
0.05% UL

YS
0.02% OFFSET

YS
0.005% OFFSET

ELONG.

RH
B

RH
C

RH
F

RH
30T

VH
500

BH
500

BH
3000

SHEAR
STRGTH

FATIGUE
STRGTH

IZOD
IMPACT
STRGTH

-

in.

%

-

F

ksi

ksi

ksi

ksi

%

B

C

F

30T

500

500

3000

ksi

ksi

ft-lb

-

mm.

-

-

C

MPa

MPa

MPa

MPa

-

-

-

-

-

-

-

-

MPa

MPa

J

FLAT PRODUCTS




















H02

0.04



68

61

50

-

-

-

-

-

-

-

-

-

-

40

-


H02

1

0

TYP

20

421

345

-

-

23

70

-

-

65

-

-

-

276

-

0

OS015

0.04



68

53

22

-

-

-

-

-

-

-

-

-

-

-

-


OS015

1

0

TYP

20

365

152

-

-

54

-

-

78

43

-

-

-

-

-

0

H06

0.04



68

85

62

-

-

-

-

-

-

-

-

-

-

45

-


H06

1

0

TYP

20

586

427

-

-

5

87

-

-

74

-

-

-

310

-

0

OS035

0.04



68

49

17

-

-

-

-

-

-

-

-

-

-

34

-


OS035

1

0

TYP

20

338

117

-

-

57

-

-

68

31

-

-

-

234

-

0

H04

0.04



68

74

60

-

-

-

-

-

-

-

-

-

-

43

14


H04

1

0

TYP

20

510

414

-

-

8

80

-

-

70

-

-

-

296

97

0

H08

0.04



68

91

62

-

-

-

-

-

-

-

-

-

-

47

20


H08

1

0

TYP

20

627

427

-

-

3

90

-

-

76

-

-

-

324

138

0

OS070

0.04



68

46

14

-

-

-

-

-

-

-

-

-

-

32

12


OS070

1

0

TYP

20

317

97

-

-

65

-

-

58

15

-

-

-

221

83

0

OS050

0.04



68

47

15

-

-

-

-

-

-

-

-

-

-

-

-


OS050

1

0

TYP

20

324

103

-

-

62

-

-

64

26

-

-

-

-

-

0

H01

0.04



68

54

40

-

-

-

-

-

-

-

-

-

-

36

-


H01

1

0

TYP

20

372

276

-

-

43

55

-

-

54

-

-

-

248

-

0

H00

0.04



68

50

35

-

-

-

-

-

-

-

-

-

-

-

-


H00

1

0

TYP

20

345

241

-

-

50

50

-

-

50

-

-

-

-

-

0

OS025

0.04



68

51

19

-

-

-

-

-

-

-

-

-

-

-

-


OS025

1

0

TYP

20

352

131

-

-

55

-

-

72

36

-

-

-

-

-

0

ROD




















H00

1



68

55

40

-

-

-

-

-

-

-

-

-

-

36

-


H00

25.4

6

TYP

20

379

276

-

-

48

55

-

-

-

-

-

-

248

-

0

OS050

1



68

48

16

-

-

-

-

-

-

-

-

-

-

34

-


OS050

25.4

0

TYP

20

331

110

-

-

65

-

-

65

-

-

-

-

234

-

0

WIRE




















H01

0.08



68

70

-

-

-

-

-

-

-

-

-

-

-

42

22


H01

2

0

TYP

20

483

-

-

-

20

-

-

-

-

-

-

-

290

152

0

H00

0.08



68

58

-

-

-

-

-

-

-

-

-

-

-

38

-


H00

2

0

TYP

20

400

-

-

-

35

-

-

-

-

-

-

-

262

-

0

H04

0.08



68

110

-

-

-

-

-

-

-

-

-

-

-

55

-


H04

2

0

TYP

20

758

-

-

-

8

-

-

-

-

-

-

-

379

-

0

H02

0.08



68

88

-

-

-

-

-

-

-

-

-

-

-

-

-


H02

2

0

TYP

20

607

-

-

-

15

-

-

-

-

-

-

-

-

-

0

H06

0.08



68

120

-

-

-

-

-

-

-

-

-

-

-

60

-


H06

2

0

TYP

20

827

-

-

-

4

-

-

-

-

-

-

-

414

-

0

H08

0.08



68

128

-

-

-

-

-

-

-

-

-

-

-

60

-


H08

2

0

TYP

20

883

-

-

-

3

-

-

-

-

-

-

-

414

-

0

OS035

0.08



68

50

-

-

-

-

-

-

-

-

-

-

-

34

-


OS035

2

0

TYP

20

345

-

-

-

60

-

-

-

-

-

-

-

234

-

0

 

Physical Properties

PRODUCT PROPERTY

US CUSTOMARY

METRIC

Coefficient of Thermal Expansion

11.3 ÌÎ?̴ÌÁ10-6 per oF (68-572 F)

20.3 ÌÎ?̴ÌÁ 10 6? per ÌÎ?̴åÁC (20-300 C)

Density

0.306 lb/in3 @ 68 F

8.47 gm/cm3 @ 20 C

Electrical Conductivity

27 %IACS @ 68 F

0.158 MegaSiemens/cm @ 20 C

Electrical Resistivity

38.4 ohms-cmil/ft @ 68 F

6.38 microhm-cm @ 20 C

Melting Point Liquid US

1710 F

932 C

Melting Point Solid US

1660 F

904 C

Modulas of Elasticity in Tension

15000 ksi

103400 MPa

Modulas of Rigidity

5600 ksi

38610 Mpa

Specific Gravity

8.47

8.47

Specific Heat Capacity

0.09 Btu/lb/ÌÎ?̴åÁF @ 68 F

377.1 J/kg ÌÎ?̴ÌÁ ÌÎ?̴åÁK at 293 K

Thermal Conductivity

67.0 Btu ÌÎ?̴ÌÁ ft/(hr ÌÎ?̴ÌÁ ft2 ÌÎ?̴ÌÁÌÎ?̴åÁF) @ 68 F

116.0 W/m ÌÎ?̴ÌÁ ÌÎ?̴åÁK at 20 C

 

 

Fabrication

JOINING TECHNIQUE

SUITABILITY

Brazing

Excellent

Butt Weld

Good

Capacity for Being Cold Worked

Excellent

Capacity for Being Hot Formed

Poor

Coated Metal Arc Welding

Not recommended

Gas Sheilded Arc Welding

Fair

Machinability rating

30

Oxyacetylene Welding

Good

Seam Weld

Not recommended

Soldering

Excellent

Spot Weld

Good


  • Name:

  • Tel:

  • Email:*

  • Whastapp/Wechat:

  • Message:*

  • SENT