Pancake Coil Copper Tube
C12000 PHOSPHORUS - DEOXIDIZED, LOW RESIDUAL P
Short Description:
C12000 copper can be performed at a temperature of about 760 to 871C (1400 to 1600°F).This alloy has good forgeability,good welding and cold bending properties.
Send email to us
Download as PDF
| Bronze, Copper & Brass Rectangular Bars (Flat Bars) | |||
| Parameter | Bronze Rectangular Bar (C93200 / C95400) | Copper Rectangular Bar (C11000 / C12200) | Brass Rectangular Bar (C36000 / C38500) |
| Material Type | Bearing Bronze / Aluminum Bronze | Electrolytic Tough Pitch (ETP) / Phosphorus Deoxidized | Free-Cutting Brass / Architectural Bronze |
| Standard | ASTM B505 / B124 | ASTM B187 / B124 | ASTM B16 / B453 |
| Thickness Range | 1/8" to 4" (3 mm to 102 mm) | 1/16" to 4" (1.6 mm to 102 mm) | 1/8" to 4" (3 mm to 102 mm) |
| Width Range | 1/4" to 12" (6 mm to 305 mm) | 1/4" to 12" (6 mm to 305 mm) | 1/4" to 12" (6 mm to 305 mm) |
| Length | 13" (330 mm) or 6.5 ft (2 m) stock | 12 ft (3.66 m) or Custom | 12 ft (3.66 m) or Custom |
| Temper Condition | As Cast / Annealed (O60) | Soft (Annealed – O60), Half-Hard (H58), Hard (H80) | Half-Hard (H02), Hard (H04) |
| Tensile Strength (Ultimate) | 35,000 – 103,000 psi (240 – 710 MPa) * | 30 – 38 ksi (210 – 260 MPa) | 48 – 65 ksi (330 – 450 MPa) |
| Yield Strength (0.5% Ext.) | 18,000 – 52,000 psi (125 – 360 MPa) * | 10 – 30 ksi (70 – 205 MPa) | 20 – 45 ksi (140 – 310 MPa) |
| Hardness (Brinell) | 65 – 220 HB * | 40 – 50 HB | 80 – 110 HB |
| Corrosion Resistance | Excellent (seawater) to Moderate * | Excellent | Good |
| Typical Applications | Wear plates, machine slides, bushings, bearing blocks, pump components, gear racks | Bus bars, grounding straps, electrical connectors, heat exchanger plates, transformer windings, gaskets | Valve plates, lock components, decorative trim, architectural hardware, screw machine parts, shims, nameplates |